1.
Compression of MgSiO3 glass in a 6/8 multianvil apparatus to 10.0 ± 0.5 GPa results in demonstrable changes in density and silicon coordination. Under high-pressure, samples were heated over a range of temperatures from 300 to 773 K, quenched to room temperature and decompressed at rates of 10.4 and 0.08 GPa/min. Recovered glasses have bulk densities that are 2.6-11.0% higher than the non-compressed glass. 29Si MAS NMR spectra of compressed glasses show narrowing of the [4]Si peak resulting from a reduction in the spread of the Si-O-Si bond angle distribution. After heating and rapid decompression, 29Si MAS NMR spectra of recovered glasses exhibit peaks assignable to [4]Si, [5]Si, and [6]Si with relative fractions of 0.945, 0.045, and 0.008, respectively. These changes in Si coordination and in Si-O-Si bond angle distribution with pressure only represent part of the structural changes associated with permanent densification of heated and unheated samples. The abundance of [6]Si is found to be insensitive to decompression rate, while [5]Si reverts to [4]Si on slow decompression at room temperature. These observations demonstrate that high-coordinated silicon species in MgSiO3 glass are formed on compression below glass transition temperatures and that pressure-induced structural changes can be preserved with rapid decompression. The ease with which [5]Si reverts to [4]Si during decompression suggests that the conversion of [4]Si → [5]Si principally involves short-range atomic displacement. The reversible and irreversible features of densification of MgSiO3 glass, provide insights into the fundamental structural and rheological properties of refractory silicate melts similar to those found in the Earth’s mantle. 相似文献
2.
We have taken a systematic approach utilizing advanced solid-state NMR techniques to gain new insights into the controversial issue concerning the dissolution mechanisms of water in aluminosilicate melts (glasses). A series of quenched anhydrous and hydrous (∼2 wt% H2O) glass samples along the diopside (Di, CaMgSi2O6)—anorthite (An, CaAl2Si2O8) join with varying An components (0, 20, 38, 60, 80, and 100 mol %) have been studied. A variety of NMR techniques, including one-dimensional (1D) 1H and 27Al MAS NMR, and 27Al → 1H cross-polarization (CP) MAS NMR, as well as two-dimensional (2D) 1H double-quantum (DQ) MAS NMR, 27Al triple-quantum (3Q) MAS NMR, and 27Al → 1H heteronuclear correlation NMR (HETCOR) and 3QMAS/HETCOR NMR, have been applied. These data revealed the presence of SiOH, free OH ((Ca,Mg)OH) and AlOH species in the hydrous glasses, with the last mostly interconnected with Si and residing in the more polymerized parts of the structure. Thus, there are no fundamental differences in water dissolution mechanisms for Al-free and Al-bearing silicate melts (glasses), both involving two competing processes: the formation of SiOH/AlOH that is accompanied by the depolymerization of the network structure, and the formation of free OH that has an opposite effect. The latter is more important for depolymerized compositions corresponding to mafic and ultramafic magmas.Aluminum is dominantly present in four coordination (AlIV), but a small amount of five-coordinate Al (AlV) is also observed in all the anhydrous and hydrous glasses. Furthermore, six-coordinate Al (AlVI) is also present in most of the hydrous glasses. As Al of higher coordinations are favored by high pressure, AlVIOH and AlVOH may become major water species at higher pressures corresponding to those of the Earth’s mantle. 相似文献
3.
Water solubility mechanism in hydrous aluminosilicate glasses: information from Al MAS and MQMAS NMR
New 27Al NMR data are presented in order to clarify the discrepancies in the interpretation of the previous 27Al Magic Angle Spinning (MAS) spectra from hydrous aluminosilicate glasses. The 27Al MAS data have been collected at much higher magnetic field (14.1 and 17.6 T) than hitherto, and in addition, multiple quantum (MQ) MAS NMR data are presented for dry and hydrous nepheline glasses and NaAlSi7.7O17.4 glass that, according to the model of Zeng et al. (Zeng Q., Nekvasil H., and Grey C. P. 2000. In support of a depolymerisation model for water in sodium aluminosilicate glasses: Information from NMR spectroscopy. Geochim. Cosmochim. Acta64, 883-896), should produce a high fraction (up to 30%) of Al in Al Q3-OH on hydration. Although small differences in the MAS spectra of anhydrous and hydrous nepheline glasses are observed, there is no evidence for the existence of significant (>∼2%) amounts of Q3 Al-OH in these glasses in either the MAS or MQMAS data. 相似文献
4.
We describe here high-field 17O magic-angle-spinning (MAS) and triple-quantum MAS (3QMAS) NMR spectra for several alkali silicate and Na, K, and Ca aluminosilicate glasses containing up to 10 wt.% water. The H2O site appears to have a large quadrupolar coupling constant, and its chemical shift increases from Na- to K- glasses, suggesting significant cation-H2O interactions. In 17O one-pulse MAS and 3QMAS and 27Al one-pulse NMR experiments, major differences were seen between spectra for anhydrous and hydrous calcium aluminosilicate glasses. The changes in the 17O MAS spectra can be explained by the addition of an H2O peak and to the disappearance of an Al-O-Al peak from the 17O NMR spectrum for the hydrous glass. The 27Al results are consistent with this interpretation. 相似文献
5.
The local configurations around sodium ions in silicate glasses and melts and their distributions have strong implications for the dynamic and static properties of melts and thus may play important roles in magmatic processes. The quantification of distributions among charge-balancing cations, including Na+ in aluminosilicate glasses and melts, however, remains a difficult problem that is relevant to high-temperature geochemistry as well as glass science.Here, we explore the local environment around Na+ in charge-balanced aluminosilicate glasses (the NaAlO2-SiO2 join) and its distribution using 23Na magic-angle spinning (MAS) nuclear magnetic resonance (NMR) spectroscopy at varying magnetic fields of 9.4, 14.1, and 18.8 T, as well as triple-quantum (3Q)MAS NMR spectroscopy at 9.4 T, to achieve better understanding of the extent of disorder around this cation. We quantify the extent of this disorder in terms of changes in Na-O distance (d[Na-O]) distributions with composition and present a structural model favoring a somewhat ordered Na distribution, called a “perturbed” Na distribution model. The peak position in 23Na MAS spectra of aluminosilicate glasses moves toward lower frequencies with increasing Si/Al ratios, implying that the average d(Na-O) increases with increasing R. The peak width is significantly reduced at higher fields (14.1 and 18.8 T) because of the reduced effect of second-order quadrupolar interaction, and 23Na MAS NMR spectra thus provide relatively directly the Na chemical shift distribution and changes in atomic environment with composition. Chemical shift distributions obtained from 23Na 3Q MAS spectra are consistent with MAS NMR data, in which deshielding decreases with R. The average distances between Na and the three types of bridging oxygens (BOs) (Na-{Al-O-Al}, Na-{Si-O-Al}, and Na-{Si-O-Si}) were obtained from the correlation between d(Na-O) and isotropic chemical shift. The calculated d(Na-{Al-O-Al}) of 2.52 Å is shorter than the d(Na-{Si-O-Si}) of 2.81 Å, and d(Na-{Al-O-Al}) shows a much narrower distribution than the other types of BOs. 23Na chemical shifts in binary (Al-free) sodium silicate glasses are more deshielded and have ranges distinct from those of aluminosilicate glasses, implying that d(Na-NBO) (nonbridging oxygen) is shorter than d(Na-BO) and that d(Na-{Si-O-Si}) in binary silicates can be shorter than that in aluminosilicate glasses. The results given here demonstrate that high-field 23Na NMR is an effective probe of the Na+ environment, providing not only average structural information but also chemically and topologically distinct chemical shift ranges (distributions) and their variation with composition and their effects on static and dynamic properties. 相似文献
6.
We studied uptake mechanisms for dissolved Al on amorphous silica by combining bulk-solution chemistry experiments with solid-state Nuclear Magnetic Resonance techniques (27Al magic-angle spinning (MAS) NMR, 27Al{1H} cross-polarization (CP) MAS NMR and 29Si{1H} CP-MAS NMR). We find that reaction of Al (1 mM) with amorphous silica consists of at least three reaction pathways; (1) adsorption of Al to surface silanol sites, (2) surface-enhanced precipitation of an aluminum hydroxide, and (3) bulk precipitation of an aluminosilicate phase. From the NMR speciation and water chemistry data, we calculate that 0.20 (±0.04) tetrahedral Al atoms nm−2 sorb to the silica surface. Once the surface has sorbed roughly half of the total dissolved Al (∼8% site coverage), aluminum hydroxides and aluminosilicates precipitate from solution. These precipitation reactions are dependent upon solution pH and total dissolved silica concentration. We find that the Si:Al stoichiometry of the aluminosilicate precipitate is roughly 1:1 and suggest a chemical formula of NaAlSiO4 in which Na+ acts as the charge compensating cation. For the adsorption of Al, we propose a surface-controlled reaction mechanism where Al sorbs as an inner-sphere coordination complex at the silica surface. Analogous to the hydrolysis of , we suggest that rapid deprotonation by surface hydroxyls followed by dehydration of ligated waters results in four-coordinate (>SiOH)2Al(OH)2 sites at the surface of amorphous silica. 相似文献
7.
Structural interaction between dissolved fluorine and silicate glass (25°C) and melt (to 1400°C) has been examined with 19F and 29Si MAS NMR and with Raman spectroscopy in the system Na2O-Al2O3-SiO2 as a function of Al2O3 content. Approximately 3 mol.% F calculated as NaF dissolved in these glasses and melts. From 19F NMR spectroscopy, four different fluoride complexes were identified. These are (1) Na-F complexes (NF), (2) Na-Al-F complexes with Al in 4-fold coordination (NAF), (3) Na-Al-F complexes with Al in 6-fold coordination with F (CF), and (4) Al-F complexes with Al in 6-fold, and possibly also 4-fold coordination (TF). The latter three types of complexes may be linked to the aluminosilicate network via Al-O-Si bridges.The abundance of sodium fluoride complexes (NF) decreases with increasing Al/(Al + Si) of the glasses and melts. The NF complexes were not detected in meta-aluminosilicate glasses and melts. The NAF, CF, and TF complexes coexist in peralkaline and meta-aluminosilicate glasses and melts.From 29Si-NMR spectra of glasses and Raman spectra of glasses and melts, the silicate structure of Al-free and Al-poor compositions becomes polymerized by dissolution of F because NF complexes scavenge network-modifying Na from the silicate. Solution of F in Al-rich peralkaline and meta-aluminous glasses and melts results in Al-F bonding and aluminosilicate depolymerization.Temperature (above that of the glass transition) affects the Qn-speciation reaction in the melts, 2Q3 ⇔ Q4 + Q2, in a manner similar to other alkali silicate and alkali aluminosilicate melts. Dissolved F at the concentration level used in this study does not affect the temperature-dependence of this speciation reaction. 相似文献
8.
9.
The heat capacity and vibrational entropy of a calcium aluminate and three peraluminous calcium aluminosilicate glasses have been determined from 2 to 300 K by heat-pulse relaxation calorimetry. Together with previous adiabatic data for six other glasses in the system CaO-Al2O3-SiO2, these results have been used to determine partial molar heat capacities and entropies for five species namely, SiO2, CaO and three different sorts of Al2O3 in which Al is 4-, 5- and 6-fold coordinated by oxygen. Given the determining role of oxygen coordination on low-temperature heat capacity, the composition independent entropies found for SiO2 and CaO indicate that short-range order around Si and Ca is not sensitive to aluminum speciation up to the highest fraction of 25% observed for VAl by NMR spectroscopy. Because of the higher room-temperature vibrational entropy of IVAl2O3 (72.8 J/mol K) compared to VAl2O3 (48.5 J/mol K), temperature-induced changes from IVAl to VAl give rise to a small negative contribution of the order of 1 J/mol K to the partial molar configurational heat capacity of Al2O3 in melts. Near 0 K, pure SiO2 glass distinguishes itself by the importance of the calorimetric boson peak. On a g atom basis, the maximum of this peak varies with the composition of calcium aluminosilicate glasses by a factor of about 2. It does not show smooth variations, however, either as a function of SiO2 content, at constant CaO/Al2O3 ratio, or as a function of Al2O3 content, at constant SiO2 content. 相似文献
10.
Frédéric Angeli Marina Gaillard Thibault Charpentier 《Geochimica et cosmochimica acta》2006,70(10):2577-2590
A multinuclear solid-state NMR investigation of the structure of the amorphous alteration products (so called gels) that form during the aqueous alteration of silicate glasses is reported. The studied glass compositions are of increasing complexity, with addition of aluminum, calcium, and zirconium to a sodium borosilicate glass. Two series of gels were obtained, in acidic and in basic solutions, and were analyzed using 1H, 29Si, and 27Al MAS NMR spectroscopy. Advanced NMR techniques have been employed such as 1H-29Si and 1H-27Al cross-polarization (CP) MAS NMR, 1H double quantum (DQ) MAS NMR and 27Al multiple quantum (MQ) MAS NMR. Under acidic conditions, 29Si CP MAS NMR data show that the repolymerized silicate networks have similar configuration. Zirconium as a second nearest neighbor increases the 29Si isotropic chemical shift. The gel porosity is influenced by the pristine glass composition, modifying the silicon-proton interactions. From 1H DQ and 1H-29Si CP MAS NMR experiments, it was possible to discriminate between silanol groups (isolated or not) and physisorbed molecular water near Si (Q2), Si (Q3), and Si (Q4) sites, as well as to gain insight into the hydrogen-bonding interaction and the mobility of the proton species. These experiments were also carried out on heated samples (180 °C) to evidence hydrogen bonds between hydroxyl groups on molecular water. Alteration in basic media resulted in a gel structure that is more dependent on the initial glass composition. 27Al MQMAS NMR data revealed an exchange of charge compensating cations of the [AlO4]− groups during glass alteration. 1H-27Al CP MAS NMR data provide information about the proximities of these two nuclei and two aluminum environments have been distinguished. The availability of these new structural data should provide a better understanding of the impact of glass composition on the gel structure depending on the nature of the alteration solution. 相似文献
11.
The structures of sodium silicate and aluminosilicate glasses quenched from melts at high pressure (6-10 GPa) with varying degrees of polymerization (fractions of nonbridging oxygen) were explored using solid-state NMR [17O and 27Al triple-quantum magic-angle spinning (3QMAS) NMR]. The bond connectivity in melts among four and highly coordinated network polyhedra, such as [4]Al, [5,6]Al, [4]Si, and [5,6]Si, at high pressure is shown to be significantly different from that at ambient pressure. In particular, in the silicate and aluminosilicate melts, the proportion of nonbridging oxygen (NBO) generally decreases with increasing pressure, leading to the formation of new oxygen clusters that include 5- and 6-coordinated Si and Al in addition to 4-coordinated Al and Si, such as [4]Si-O-[5,6]Si, [4]Si-O-[5,6]Al and Na-O-[5,6]Si. While the fractions of [5,6]Al increase with pressure, the magnitude of this increase diminishes with increasing degrees of ambient-pressure polymerization under isobaric conditions. Incorporating the above structural information into models of melt properties reproduces the anomalous pressure-dependence of O2− diffusivity and viscosity often observed in silicate melts. 相似文献
12.
In order to decipher information about the local coordination environments of Na in anhydrous silicates from 23Na nuclear magnetic resonance spectroscopy (NMR), we have collected 23Na magic angle spinning (MAS) NMR spectra on several sodium-bearing silicate and aluminosilicate crystals with known structures. These data, together with those from the literature, suggest that the 23Na isotropic chemical shift correlates well with both the Na coordination and the degree of polymerization (characterized by NBO/T) of the material. The presence of a dissimilar network modifier also affects the 23Na isotropic chemical shift. From these relations, we found that the average Na coordinations in sodium silicate and aluminosilicate liquids of a range of compositions at 1 bar are nearly constant at around 6–7. The average Na coordinations in glasses of similar compositions also vary little with Na content (degree of polymerization). However, limited data on ternary alkali silicate and aluminosilicate glasses seem to suggest that the introduction of another network-modifier, such as K or Cs, does cause variations in the average local Na coordination. Thus it appears that the average Na coordination environments in silicate glasses are more sensitive to the presence of other network-modifiers than to the variations in the topology of the silicate tetrahedral network. Further studies on silicate glasses containing mixed cations are necessary to confirm this conclusion. 相似文献
13.
Travis O. Sandland Jonathan F. Stebbins James D. Webster 《Geochimica et cosmochimica acta》2004,68(24):5059-5069
Chlorine-35 magic angle spinning (MAS) nuclear magnetic resonance (NMR) spectra were collected at 14.1 and 18.8 Tesla fields to determine the atomic scale structural environments of the chloride ions in anhydrous and hydrous silicate and aluminosilicate glasses containing 0.2 to 0.7 wt% Cl. NMR peaks are broad and featureless, but are much narrower than the total chemical shift range for the nuclide in inorganic chlorides. Peak widths are primarily due to quadrupole interactions and to a lesser extent to chemical shift distributions. Peak positions are quite different for the Na- and Ca-containing glasses, suggesting that most Cl− coordination environments contain network modifier cations. Comparison of peak positions and shapes for silicate and aluminosilicate glasses containing either Na or Ca suggests that there is no obvious contribution from Cl− bonded to Al, and relative quantitation of peak areas indicates that there is no systematic undercounting of 35Cl spins in the aluminous vs. the Al-free samples. In Ca-Na silicate glasses with varying Ca/(Ca + Na), the mixed-cation glasses have intermediate chemical shifts between those of the end members, implying that there is not a strong preference of either Ca2+ or of Na+ around Cl−. Hydrous Na-aluminosilicate glasses with H2O contents up to 5.9 wt% show a shift to higher frequency NMR signal with increasing H2O content, while the quadrupole coupling constant (CQ) remains constant at ∼3.3 MHz. However, the change in frequency is much smaller than that expected if H2O systematically replaced Na+ in the first-neighbor coordination shell around Cl−. A series of hydrous Ca-aluminosilicate glasses with H2O contents up to 5.5 wt% show no shift in NMR signal with increasing H2O content. The CQ remains constant at ∼4.4 MHz, again suggesting no direct interaction between Cl− and H2O in these samples. 相似文献
14.
Jonathan F. Stebbins Emily V. Dubinsky Koji Kanehashi Kimberly E. Kelsey 《Geochimica et cosmochimica acta》2008,72(3):910-925
Configurational changes with temperature are important for the thermodynamic and transport properties of most aluminosilicate melts, but in general are not well understood. Here, we present high-resolution 27Al and 17O NMR data on several calcium aluminosilicate glasses prepared with varying quench rates and thus with fictive temperatures that span ranges up to about 200 K. In all compositions the content of five-coordinated aluminum increases with fictive temperature, in agreement with recent high temperature NMR data on melts. In a glass of CaAl2Si2O8 (“anorthite”) composition, the content of non-bridging oxygens also increases with temperature; however this effect was not observed in a sample with a much higher CaO/Al2O3 ratio. We present a consistent notation for reactions among structural species in these systems that clarify why in some cases, high-coordinated network cations may appear on the same side of the reaction, while in others they occur on the opposite sides: the key difference is in accounting for all coordination changes for oxygens. Mixing of non-bridging oxygens and of high-coordinated aluminum make significant contributions to the overall configurational entropy and heat capacity of the melts, as does the mixing of various bridging oxygens and of tetrahedral network cations. Other, less well known, types of increase in disorder with temperature may be important as well. 相似文献
15.
Estimation of the framework connectivity and the atomic structure of depolymerized silicate melts and glasses (NBO/T > 0) remains a difficult question in high-temperature geochemistry relevant to magmatic processes and glass science. Here, we explore the extent of disorder and the nature of polymerization in binary Ca-silicate and ternary Ca-aluminosilicate glasses with varying NBO/T (from 0 to 2.67) using O-17 NMR at two different magnetic fields of 9.4 and 14.1 T in conjunction with quantum chemical calculations. Non-random distributions among framework cations (Si and Al) are demonstrated in the variation of relative populations of oxygen sites with NBO/T. The proportion of non-bridging oxygen (NBO, Ca-O-Si) in the binary and ternary aluminosilicate glasses increases with NBO/T. While the trend is consistent with predictions from composition, the detailed fractions apparently deviate from the predicted values, suggesting further complications in the nature of polymerization. The proportion of each bridging oxygen in the glasses also varies with NBO/T. The fractions of Al-O-Si and Al-O-Al increase with increasing polymerization as CaO is replaced with Al2O3, while that of Si-O-Si seems to decrease, implying that activity of silica may decrease from calcium silicate to polymerized aluminosilicates (XSiO2=constant). Quantum chemical molecular orbital calculations based on density functional theory show that a silicate chain with Al-NBO (Ca-O-Al) has an energy penalty (calculated cluster energy difference) of about 108 kJ/mol compared with the cluster with Ca-O-Si, consistent with preferential depolymerization of Si-networks, reported in an earlier O-17 NMR study [Allwardt, J., Lee, S.K., Stebbins, J.F., 2003. Bonding preferences of non-bridging oxygens in calcium aluminosilicate glass: Evidence from O-17 MAS and 3QMAS NMR on calcium aluminate glass. Am. Mineral.88, 949-954]. These prominent types of non-randomness in the distributions suggest significant chemical order in silicate glasses that leads to a decrease in silica activity coefficient and will be useful in modeling transport properties of melts. 相似文献
16.
Water speciation in rhyolitic melts with dissolved water ranging from 0.8 to 4 wt% under high pressure was investigated. Samples were heated in a piston-cylinder apparatus at 624-1027 K and 0.94-2.83 GPa for sufficient time to equilibrate hydrous species (molecular H2O and hydroxyl group, H2Om + O ? 2OH) in the melts and then quenched roughly isobarically. The concentrations of both hydrous species in the quenched glasses were measured with Fourier transform infrared (FTIR) spectroscopy. For the samples with total water content less than 2.7 wt%, the equilibrium constant (K) is independent of total H2O concentration. Incorporating samples with higher water contents, the equilibrium constant depends on total H2O content, and a regular solution model is used to describe the dependence. K changes with pressure nonmonotonically for samples with a given water content at a given temperature. The equilibrium constant does not change much from ambient pressure to 1 GPa, but it increases significantly from 1 to 3 GPa. In other words, more molecular H2O reacts to form hydroxyl groups as pressure increases from 1 GPa, which is consistent with breakage of tetrahedral aluminosilicate units due to compression of the melt induced by high pressure. The effect of 1.9 GPa (from 0.94 to 2.83 GPa) on the equilibrium constant at 873 K is equivalent to a temperature effect of 49 K (from 873 K to 922 K) at 0.94 GPa. The results can be used to evaluate the role of speciation in water diffusion, to estimate the apparent equilibrium temperature, and to infer viscosity of hydrous rhyolitic melts under high pressure. 相似文献
17.
Revealing the atomic structure and disorder in oxide glasses, including sodium silicates and aluminosilicates, with varying degrees of polymerization, is a challenging problem in high-temperature geochemistry as well as glass science. Here, we report 17O MAS and 3QMAS NMR spectra for binary sodium silicate and ternary sodium aluminosilicate glasses with varying degrees of polymerization (Na2O/SiO2 ratio and Na2O/Al2O3 ratio), revealing in detail the extent of disorder (network connectivity and topological disorder) and variations of NMR parameters with the glass composition. In binary sodium silicate glasses [Na2O-k(SiO2)], the fraction of non-bridging oxygens (NBOs, Na-O-Si) increases with the Na2O/SiO2 ratio (k), as predicted from the composition. The 17O isotropic chemical shifts (17O δiso) for both bridging oxygen (BO) and NBO increase by about 10-15 ppm with the SiO2 content (for k = 1-3). The quadrupolar coupling products of BOs and NBOs also increase with the SiO2 content. These trends suggest that both NBOs and BOs strongly interact with Na; therefore, the Na distributions around BOs and NBOs are likely to be relatively homogenous for the glass compositions studied here, placing some qualitative limits on the extent of segregation of alkali channels from silica-enriched regions as suggested by modified random-network models. The peak width (in the isotropic dimension) and thus bond angle and length distributions of Si-O-Si and Na-O-Si increase with the SiO2 content, indicating an increase in the topological disorder with the degree of polymerization. In the ternary aluminosilicate glasses [Na2O]x[Al2O3]1−xSiO2, the NBO fraction decreases while the Al-O-Si and Al-O-Al fractions apparently increase with increasing Al2O3 content. The variation of oxygen cluster populations suggests that deviation from “Al avoidance” is more apparent near the charge-balanced join (Na/Al = 1). The Si-O-Si fraction, which is closely related to the activity coefficient of silica, would decrease with increasing Al2O3 content at a constant mole fraction of SiO2. Therefore, the activity of silica may decrease from depolymerized binary silicates to fully polymerized sodium aluminosilicate glasses at a constant mole fraction of SiO2. 相似文献
18.
B.H.W.S. de Jong Charles M. Schramm Victor E. Parziale 《Geochimica et cosmochimica acta》1983,47(7):1223-1236
The coordination of aluminum with oxygen in crystalline and amorphous alumina, aluminates, and aluminosilicates has been determined with magic angle spinning 27Al nuclear magnetic resonance. The 27Al NMR spectra of crystalline materials show that VIAl and IVAl can readily be distinguished. The same is not the case for amorphous aluminosilicates due to the superposition of a narrow peak, characteristic of IVAl, on a broad band. Our spectroscopic results indicate that Al coordination is not the determining factor in explaining differences in devitrification behavior of albite and anorthite glasses. The coordination of Al in aqueous solutions seems to prevent precipitation of the three common Al(OH)3 polymorphs (VIAl) at pH above 10. There is clear evidence to suggest that, in solutions containing Si as well as Al, aluminum coordination is related to the type of precipitate formed in acid (clays, VIAl, IVAl), and basic (zeolites, IVAl) environments. Zeolites can be precipitated in near neutral pH environments at higher temperatures, reflecting an increase in IVAl under these conditions. The Al avoidance principle for aluminosilicates does not seem to be a hard principle. It is likely that the validity of this principle depends on the type of modifying cation present in the aluminosilicate framework. 相似文献
19.
Tecto-aluminosilicate and peraluminous glasses have been prepared by conventional and laser heating techniques, respectively, in the CaO-Al2O3-SiO2 system. The structure of these glasses were studied using Raman spectroscopy, X-ray absorption at the Al K-edge and 27Al NMR spectroscopy with two different high fields (400 and 750 MHz). Raman spectroscopy and X-ray absorption are techniques sensitive to the network polymerization and, in particular, show different signal as a function of silica content. However, these two techniques are less sensitive than NMR to describe the local aluminium environment. For tectosilicate glasses, aluminium in five-fold coordination, [5]Al, was found and a careful quantification allows the determination of a significant amount of [5]Al (7% in the anorthite glass). The proportion of [5]Al increases for the peraluminous glasses with small amounts (<2%) of six-fold coordination, [6]Al. The presence of [5]Al agrees with previous observations of the existence of nonbridging oxygens (NBOs) in tectosilicate compositions. However, the proportion of [5]Al in the present study indicates that no major proportion of triclusters (oxygen coordinated to three (Si,Al)O4 tetrahedra) is required to explain these NBOS. 相似文献
20.
C. I. Sainz-Díaz J. Cuadros A. Hernández-Laguna 《Physics and Chemistry of Minerals》2001,28(7):445-454
An inverse Monte Carlo (MC) method was developed to determine the distribution of octahedral cations (Al3+, Fe3+, and Mg2+) in bentonite illite–smectite (I–S) samples (dioctahedral 2:1 phyllosilicates) using FT–IR and 27Al MAS NMR spectroscopies. FT–IR allows determination of the nature and proportion of different cation pairs bound to OH groups measuring the intensities of OH-bending bands. 27Al MAS NMR data provide information about cation configuration because 27Al MAS NMR intensity depends on Fe distribution. MC calculations based on FT–IR data alone show Fe segregation by short-range ordering (Fe clusters within 9 to 15?Å from a given Fe atom). Fe segregation increases with illite proportion. MC calculations based on IR and 27Al NMR simultaneously yield similar configurations in which Fe clusters are smaller. The latter calculations fail to build appropriate cation distributions for those samples with higher number of illite layers and significant Fe content, which is indicative of long-range Fe ordering that cannot be detected by FT–IR and 27Al MAS NMR. The proportion of Mg–Mg pairs is negligible in all samples, and calculations, in which the number of Mg atoms, as second neighbours, is minimised, create appropriate configurations. 相似文献