共查询到20条相似文献，搜索用时 288 毫秒
1.
Cracking and coalescence behavior in a rectangular rock-like specimen containing two parallel (stepped and coplanar) pre-existing open flaws under uniaxial compression load has been numerically studied by a parallel bonded-particle model, which is a type of bonded-particle model. Crack initiation and propagation from two flaws replicate most of the phenomena observed in prior physical experiments, such as the type (tensile/shear) and the initiation stress of the first crack, as well as the coalescence pattern. Eight crack coalescence categories representing different crack types and trajectories are identified. New coalescence categories namely “New 1” and “New 2”, which are first observed in the present simulation, are incorporated into categories 3 and 4, and category 5 previously proposed by the MIT Rock Mechanics Research Group, respectively. The flaw inclination angle (β), the ligament length (L) (spacing between two flaws) and the bridging angle (α) (inclination of a line linking up the inner flaw tips, between two flaws) have different effects on the coalescence patterns, coalescence stresses (before, at or post the peak stress) as well as peak strength of specimens. Some insights on the coalescence processes, such as the initiation of cracks in the intact part of specimens at a distance away from the flaw tips, and coalescence due to the development and linkage of a number of steeply inclined to vertical macro-tensile cracks are revealed by the present numerical study. 相似文献
2.
An Experimental Study of Crack Coalescence Behaviour in Rock-Like Materials Containing Multiple Flaws Under Uniaxial Compression 总被引：4，自引：1，他引：3
Experiments on man-made flawed rock-like materials are applied extensively to study the mechanical behaviour of rock masses as well as crack initiation modes and crack coalescence types. A large number of experiments on specimens containing two or three pre-existing flaws were previously conducted. In the present work, experiments on rock-like materials (formed from a mixture of sand, plaster, limestone and water at mass ratio of 126:9:9:16) containing multiple flaws subjected to uniaxial compression were conducted to further research the effects of the layout of pre-existing flaws on mechanical properties, crack initiation modes and crack coalescence types. Compared with previous experiments in which only three types of cracks were found, the present experiments on specimens containing multiple flaws under uniaxial compression revealed five types of cracks, including wing cracks, quasi-coplanar secondary cracks, oblique secondary cracks, out-of-plane tensile cracks and out-of-plane shear cracks. Ten types of crack coalescence occurred through linkage among wing cracks, quasi-coplanar secondary cracks, oblique secondary cracks, out-of-plane shear cracks and out-of-plane tensile cracks. Moreover, the effects of the non-overlapping length and flaw angle on the complete stress–strain curves, the stress of crack initiation, the peak strength, the peak strain and the elastic modulus were also investigated in detail. 相似文献
3.
Cracking processes have been extensively studied in brittle rock and rock-like materials. Due to the experimental limitations and the complexity of rock texture, details of the cracking processes could not always be observed and assessed comprehensively. To contribute to this field of research, a numerical approach based on the particle element model was used in present study. It would give us insights into what is happening to crack initiation, propagation and coalescence. Parallel bond model, a type of bonded-particle model, was used to numerically simulate the cracking process in rock-like material containing a single flaw under uniaxial vertical compression. The single flaw’s inclinations varied from 0° to 75° measured from the horizontal. As the uniaxial compression load was increased, multiple new microcracks initiated in the rock, which later propagated and eventually coalesced into longer macrocracks. The inclination of the pre-existing flaw was found to have a strong influence on the crack initiation and propagation patterns. The simulations replicated most of the phenomena observed in the physical experiments, such as the type, the initiation location and the initiate angle of the first cracks, as well as the development of hair-line cracks, which later evolved to macrocracks. Analyses of the parallel bond forces and displacement fields revealed some important mechanisms of the cracking processes. The first cracks typically initiated from the tensile stress concentration regions, in which the tensile stress was partially released after their initiation. The tensile stress concentration regions subsequently shifted outwards close to the propagating tips of the first cracks. The initiation and propagation of the first cracks would not significantly influence the compressive stress singularity at the flaw tips, which was the driving force of the initiation of secondary cracks. The initiation of microcracking zone consisting almost exclusively of micro-tensile cracks, and that of microcracking zone consisting of micro-tensile cracks and mixed micro-tensile and shear cracks, were found to be correlated with two distinct types of displacement fields, namely type I (DF_I) and type II (DF_II), respectively. 相似文献
4.
A 3-D conjugated bond-pair-based peridynamic model is developed to comprehensively investigate failure characteristics of rock-like materials with intermittent fissures in the compressive-shear loading tests. Rock-like specimens containing one single central fissure are first simulated. Numerical results indicate that the 3-D conjugated bond-pair-based peridynamic model can faithfully reproduce failure characteristics of rock-like materials under compressive-shear loads. Then, the failure characteristics of rock-like specimens containing two parallel central intermittent fissures are numerically investigated. Effects of fissure inclination angle, fissure ligament length and rock bridge angle on fracturing behaviors, such as crack coalescence patterns, are also studied as well as crack initiation stress and coalescence stress.
相似文献5.
Crack Coalescence in Molded Gypsum and Carrara Marble: Part 1. Macroscopic Observations and Interpretation 总被引：8，自引：5，他引：3
Cracking and coalescence behavior has been studied experimentally with prismatic laboratory-molded gypsum and Carrara marble
specimens containing two parallel pre-existing open flaws. This was done at both the macroscopic and the microscopic scales, and the results are presented in two separate papers. This paper (the first of two) summarizes the macroscopic experimental
results and investigates the influence of the different flaw geometries and material, on the cracking processes. In the companion
paper (also in this issue), most of the macroscopic deformation and cracking processes shown in this present paper will be
related to the underlying microscopic changes. In the present study, a high speed video system was used, which allowed us
to precisely observe the cracking mechanisms. Nine crack coalescence categories with different crack types and trajectories
were identified. The flaw inclination angle (β), the ligament length (L), that is, intact rock length between the flaws, and the bridging angle (α), that is, the inclination of a line linking up the inner flaw tips, between two flaws, had different effects on the coalescence
patterns. One of the pronounced differences observed between marble and gypsum during the compression loading test was the
development of macroscopic white patches prior to the initiation of macroscopic cracks in marble, but not in gypsum. Comparing
the cracking and coalescence behaviors in the two tested materials, tensile cracking generally occurred more often in marble
than in gypsum for the same flaw pair geometries.
相似文献
| H. H. EinsteinEmail: |
6.
The present numerical study, which is an extension of our previous numerical analysis on cracking processes of a single pre-existing flaw, focuses on the coalescence of two pre-existing parallel open flaws in rock subjected to a uniaxial compressive loading. To facilitate a systematic investigation, the arrangements of the flaw pair are classified into 11 categories. Simulations engaging AUTODYN are conducted on each category. The numerical results are compared with some published physical experimental test results. Eleven typical coalescence patterns are obtained, which are in good agreement with the experimental results, which include two coalescence patterns obtained in flaw pair arrangements (II) and (VIII″) not being reported in previous studies. The information gathered in the simulations helps identify the type (tensile/shear) of each crack segment involved in the coalescence. Most of the coalescence cracks initiate at or around the flaw tips, except those in flaw pair arrangements (II) and (IX′) with a very short ligament length, in which the coalescence cracks initiate on the flaw surfaces away from the flaw tip regions. Based on the numerical simulation results, the properties of the 11 coalescence patterns are obtained. Except those in flaw pair arrangements (II) and (IX′), the other coalescence patterns can be interpreted with respect to the basic crack types—tensile wing crack, horsetail crack and anti-wing crack. In addition, based on the type of crack segments involved in coalescence, namely tensile and shear, the coalescence can be classified into T mode (tensile mode), S mode (shear mode) and TS mode (mixed tensile–shear mode). 相似文献
7.
在传统键基近场动力学模型的基础上,提出可以反映岩石类材料应力-应变变化特点的改进型模型,弥补了传统近场动力学模型在模拟岩石类材料时无法反映岩石内应力随应变先增加再减小最后破坏这一特性的不足。运用改进型模型,对含有单裂纹试件在不同预制裂纹角度及拉伸荷载条件下的裂纹扩展过程进行了数值模拟,分析了开裂角度在不同预制裂纹角度及拉伸荷载条件下的变化。结果表明：预制角度及拉伸荷载对开裂角度都有影响,在试件周围拉荷载接近的情况下会获得较小的开裂角,并且在拉荷载一定的条件下开裂角会有先增加后减少的规律。同时模拟了含裂纹岩石在单轴压缩条件下的裂纹扩展情况,将数值模拟的结果与室内试验的结果对比,验证了所提出新模型的有效性。所提出的新模型可以较好地模拟岩石类材料在拉荷载条件下的力学特性,在岩石数值模拟方面有着较为广泛的应用前景。 相似文献
8.
Crack evolution is initiated by the occurrence of tensile wing cracks and is then further promoted due to the crack coalescence caused by the extension of a central tensile crack segment between two relatively adjacent flaws. To understand such progressive failures in rock, a parallelized peridynamics coupled with a finite element method is utilized. Through this method, the initiation position of tensile wing cracks is observed with respect to varying inclination angles of a flaw, and then its corresponding shifting mechanism is investigated. In addition, the phenomenon of the position shifting being sensitive to various flaw shapes is discussed. Moreover, it is observed that the inclination angle of a central flaw affects the initiation position of other flaws; therefore, the initiation positions of tensile wing crack emanating from other neighboring flaws are analyzed with their angles. Following tensile wing cracks, a central tensile crack segment occurs in the bridging region between a central flaw and other neighboring flaws; the developmental patterns caused by the crack segment are discussed as well. Finally, the role a central tensile crack segment plays in the formation of crack coalescence and specimen failure is investigated in detail. The numerical results in this paper demonstrate good fidelity with established physical test results and complement them, thereby expanding the understanding of fracturing morphology in rock specimens with various flaws. 相似文献
9.
Preexisting flaws and rock heterogeneity have important ramifications on the process of rock fracturing and on rock stability in many applications. Therefore, there is great interest in numerical modelling of rock fracture and the underlying mechanisms. We simulated damage evolution and fracture propagation in sandstone specimens containing a preexisting 3-D surface flaw under uniaxial compression. We applied the linear elastic damage model based on the unified strength theory following the rock failure process analysis code. However, in contrast to the rock failure process analysis code, we used the finite element method with tetrahedron elements on unstructured meshes. It provided higher geometrical flexibility and allowed for a more accurate representation of the disk-shaped flaw with various flaw depths, angles, and lengths through locally adapted meshes. The rock heterogeneity was modelled by sampling the initial local Young's modulus from a Weibull distribution over a cubic grid. The values were then interpolated to the computational finite element method mesh. This method introduced an additional length scale for the rock heterogeneity represented by the cell size in the sampling grid. The generation of three typical surface cracking patterns, called wing cracks, anti-wing cracks, and far-field cracks, were identified in the simulation results. These depend on the geometry of the preexisting surface flaw. The simulated fracture propagation, coalescence types, and failure modes for the specimens with preexisting surface flaw show good agreement with recent experimental studies. 相似文献
10.
Cracks and joints are common in rock masses and play a crucial role in rock mass stability. This study prepared specimens with multiple parallel pre-existing flaws by embedding iron sheets in rock-like materials and used the samples to investigate the crack growth characteristics of these materials. Biaxial compression experiments were performed on sixty specimens, and the influences of the number of pre-existing flaws, their angles and the lateral stress on crack growth were investigated based on video recordings of the crack growth. The results demonstrate that structural failure will occur due to crack growth when the sample contains a small number of pre-existing flaws and that as the number of cracks increases, the specimens will fail due to local failures. In addition, the types of rock bridge failures are summarized, including wing cracks, secondary shear cracks between horizontally-separated pre-existing flaws and secondary shear cracks between vertically-separated pre-existing flaws. Wing cracks play a significant role in the failure of the specimens. The results increase the understanding of crack growth in brittle materials that contain multiple parallel pre-existing flaws under biaxial compression. 相似文献
11.
This paper investigates the influence of a flaw on crack initiation, the failure mode, deformation field and energy mechanism of the rock-like material under uniaxial compression. The results of laboratory test and numerical simulation demonstrate the flaw inclination effect can be classified into three groups: 0–30°, 30–60° and 75–90°. The characteristic stresses increase as the flaw angle increases. The tensile cracks initiate from gentle flaws (α ⩽ 30°) and shear cracks appear at tips of steep flaws (α ⩾ 45°). The input energy, strain energy and dissipation energy of a specimen show approximate increasing trends as the flaw angle increases. 相似文献
12.
脆性岩石材料在压应力作用下常出现两类裂纹：翼型张拉裂纹和次生剪切裂纹。近场动力学是一种新型的无网格数值计算方法。在近场动力学理论中,采用积分形式的控制方程代替微分形式的控制方程使得该数值算法在断裂问题上具有独特的优势。将Mohr-Coulomb准则和最大主应力准则引入非普通“态”基近场动力学理论中,分别用于模拟材料常见的压剪和张拉破坏。这种扩展的非普通“态”基近场动力学可以有效地模拟脆性岩石材料在多种受力状态下的裂纹起裂、扩展和连接问题。通过5个不同的数值算例说明该数值算法在处理脆性岩石材料断裂问题的有效性和准确性。首先,通过模拟含圆孔的弹性板拉伸数值试验说明该数值算法的有效性和准确性。其次,数值模拟了简单三点弯曲试验以及不使用其他外部准则条件下动荷载作用下裂纹的分叉试验,所得结果与其他试验结果或数值结果相吻合,从而验证了该理论的有效性。然后,模拟了包含斜裂纹的巴西圆盘试验,裂纹扩展路径和计算所得的断裂韧度同样吻合于试验结果。最后,模拟了单轴压缩状态下,预制裂纹试样的裂纹扩展和连接问题。将该数值算法与试验结果对比表明,所提出的数值方法可以模拟和预测岩石类材料的张拉和压剪裂纹的起裂、扩展和连接行为。 相似文献
13.
揭示双轴循环荷载条件下类玄武岩内裂纹起裂、扩展及岩桥贯通模式。配制类玄武岩相似材料,预制裂纹倾角=30、裂纹长度2a=20mm、裂纹厚度l=0.3mm的双裂纹,设计不同岩桥长度L、岩桥倾角试样,采用双轴压缩、双轴循环加卸载方式,研究裂纹扩展及岩桥贯通模式。试验结果表明:(1)双轴循环加卸载条件下,裂纹扩展-岩桥贯通过程可分为翼裂纹起裂、翼裂纹扩展和次生裂纹起裂及扩展、岩桥贯通3个阶段;(2)岩桥贯通类型可分为剪性贯通、张剪复合贯通和张性贯通3类。双轴压缩条件下,岩桥贯通模式可进一步划分为9种模式,双轴循环加卸载条件下,岩桥贯通模式可分为8种模式;(3)双轴循环加卸载试验比双轴压缩试验更易发生剪性贯通,且在部分试样岩桥处出现局部压碎隆起现象;(4)岩桥倾角和岩桥长度L对岩桥贯通模式影响显著,随着岩桥倾角的增大,岩桥贯通模式逐渐转变为剪性或张剪性贯通。双轴压缩条件下,岩桥长度增加,贯通模式由张剪复合贯通过渡为剪性贯通,而双轴循环加卸载试验则恰恰相反。 相似文献
14.
Three-dimensional surface crack initiation and propagation in two kinds of heterogeneous rocks were numerically investigated via parallel finite element analysis using a supercomputer. Numerically simulated rock specimens containing a pre-existing flaw were subjected to uniaxial compression until failure. The initiation and propagation of wing cracks, anti-wing cracks, and shell-like cracks were reproduced by numerical simulations. The numerically simulated results demonstrate that the further propagation of wing cracks and shell-like cracks stop due to their wrapping (curving) behavior in three-dimensional spaces, even if the applied loads continue to increase. Furthermore, rock heterogeneity could significantly influence crack propagation patterns and the peak uniaxial compressive strengths of rock specimens. Moreover, anti-wing cracks only appeared in relatively heterogeneous rocks, and the peak uniaxial compressive strengths of the specimens were observed to depend on the inclination of the pre-existing flaw. Finally, the mechanism of surface crack propagation is discussed in the context of numerically simulated anti-plane loading tests, wherein it was identified that Mode III loading (anti-plane loading) does not lead to Mode III fracture in rocks due to their high ratio of uniaxial compressive strength to tensile strength. This finding could explain the lateral growth of an existing flaw in its own plane, which is a phenomenon that has not been observed in laboratory experiments. 相似文献
15.
共面非贯通裂隙的贯通机制对于确定外载下岩质边坡的滑动面位置及滑动面综合抗剪强度至关重要。采用预制共面非贯通裂隙石膏模型试样单轴静动载对比试验,对不同裂隙倾角共面排列裂隙的扩展、贯通过程进行了观测,研究显示：共面非贯通裂隙不同倾角下的贯通模式存在较大差异,裂隙倾角为0o～35o时以裂隙面发生闭合变形为主;45o～65o时裂隙间较易出现剪切型破坏模式;75o～90o预制裂隙面较难产生滑动,裂隙试样主要产生劈裂形式的破坏。动载下预制裂隙试样裂尖翼裂纹及次生共面裂纹起裂后易朝原起裂方向快速发展;易在两预制裂隙内端部产生直接贯通,这与静载下岩桥处的贯通常通过分支裂纹拐折扩展、相连不同。含共面非贯通裂隙试样在裂隙倾角为35o左右时强度呈现最小值,这与贯通性裂隙试样裂隙倾角为60o左右呈现最小值相差较大,这是因为裂隙面摩擦强度没来得及发挥作用所致。因此,含非贯通节理裂隙岩体的综合抗剪强度公式应引入强度发挥系数,以充分考虑岩桥胶结强度与裂隙面摩擦强度不能同步发挥作用的破坏本质。 相似文献
16.
为了研究不同倾角下多节理岩体力学行为,采用10 MN微机控制电液伺服大型多功能动静力三轴仪,开展包含较多预制非贯通节理类岩石试件的单轴压缩试验,研究了多节理岩体裂纹的特征、贯通模式、破坏模式、应力-应变特征等与节理倾角之间的关系。试验结果表明,（1）多节理岩体的裂纹类型主要有翼裂纹和次生共面裂纹,翼裂纹的扩展路径与单个节理情况下的扩展路径差异较大,翼裂纹起裂后沿起裂方向存在较长的扩展长度,直接与相邻节理或翼裂纹形成贯通,并且裂纹的贯通表现出四种不同的模式;（2）多节理岩体的破坏模式归纳为3种类型：平面破坏、块体转动式破坏和台阶式破坏;（3）根据多节理岩体的应力-应变曲线在应变软化阶段所表现出的不同非线性变形行为特征,可以将曲线归纳为4种类型;（4）多节理岩体的强度和变形各向异性特征非常显著,强度和弹性模量均在节理倾角30°时最小,90°时最大。 相似文献
17.
对含预制裂纹的花岗岩进行单轴压缩试验研究预制裂纹倾角α对脆性岩石渐进性破坏过程的影响。首先埘破坏过程的轴向应力-横向应变曲线进行总结和讨论,然后分析预制裂纹与加载方向夹角α埘岩石的应应力门槛值：裂纹起始应力σci、裂纹扩展应力σed、峰值强度矿σf,由应变片记录的应力-应变曲线和试样的表嘶裂纹扩展情况的影响机制。结果表明,含有预制裂纹的岩石试样进行加载试验过程中,顶制裂纹倾角α的变化成了决定脆性岩石破裂办式的主要因素。故在对含节理、裂隙的脆性岩石的工程应用上,通过对岩休的轴向应力-横向应变向应变典线进行分析,可以对地下开挖工程起到指导设计开挖方式及支护形式的作用。 相似文献
18.
An Experimental Study of the Fracture Coalescence Behaviour of Brittle Sandstone Specimens Containing Three Fissures 总被引：9，自引：6，他引：3
S. Q. Yang D. S. Yang H. W. Jing Y. H. Li S. Y. Wang 《Rock Mechanics and Rock Engineering》2012,45(4):563-582
To analyse the fracture coalescence behaviour of rock, rectangular prismatic sandstone specimens (80?×?160?×?30?mm in size) containing three fissures were tested under uniaxial compression. The strength and deformation behaviours of the specimens are first analysed by investigating the effects of the ligament angle β2 on the peak strength, peak strain and crack initiation stress of the specimens. To confirm the sequence of crack coalescence, a photographic monitoring technique is used throughout the entire period of deformation. Based on the results, the relationship between the real-time crack coalescence process and the axial stress–strain curve of brittle sandstone specimens is also developed, and this relationship can be used to evaluate the macroscopic deformation characteristics of pre-cracked rock. The equivalent strain evolution fields of the specimen, with α?=?β1?=?45° and β2?=?90°, are obtained using the digital image correlation technique and show good agreement with the experimental results of pre-cracked brittle sandstone. These experimental results are expected to improve the understanding of fracture mechanisms and be used in rock engineering with intermittent structures, such as deep underground excavated tunnels. 相似文献
19.
单轴压缩条件下裂隙岩样冻融损伤破坏模式分析 总被引：8，自引：7，他引：1
以寒区裂隙岩体为研究对象,采用水泥砂浆类岩石材料制作具有不同几何特征的裂隙岩样,对预制的不同裂隙岩样进行冻融循环试验和单轴压缩试验,研究裂隙长度、裂隙倾角、裂隙数目以及冻融循环次数对试件贯通模式的影响。试验表明：裂隙岩体的几何特征以及冻融循环作用对岩体损伤破坏模式有较大影响。随着冻融循环次数的增加,岩样破裂面的破裂程度越来越严重,破坏模式也越来越复杂;裂隙倾角为30°的裂隙岩样,主要发生拉伸破坏,而裂隙倾角为60°的裂隙岩样,则表现为拉剪贯通,且双裂隙岩样岩桥间多出现压剪裂纹,对于裂隙倾角为90°的岩样,裂隙数目以及裂隙长度对其影响不大,均为劈裂破坏,且破坏面不一定为裂隙面;预制裂隙长度越大,越容易产生除了主拉裂纹以外的支裂纹（压裂纹）。研究结果可为寒区岩体工程建设及运营提供科学的参考。 相似文献
20.
选用环氧树脂和纯水泥浆作为注浆材料,对含不同角度和不同注浆材料裂隙试样进行单轴压缩试验。试验结果表明,注浆材料和裂纹缺陷角度对类岩石试件单轴抗压强度及破坏模式具有重要影响;环氧树脂加固效果优于纯水泥浆,环氧树脂可以有效地消除预制裂纹尖端的应力集中;在裂纹缺陷角度很小( <30°)和角度很大( =90°)的情况下无论裂隙是注环氧树脂还是纯水泥浆,注浆效果都不明显,当 =60°时两种注浆材料的加固效果都很好。提出滑动裂纹模型,对注浆裂隙进行力学分析发现,含注浆裂隙试样的抗压强度随着注浆材料和完整材料胶结面摩擦系数和黏聚力的增大而增大,不同注浆材料和完整材料胶结面的摩擦系数和黏聚力不同,解释了为什么不同的注浆材料对注浆试样强度提升作用不同。研究成果为分析工程中注浆材料和裂纹缺陷角度对岩体强度的影响提供了一定的理论基础。 相似文献