Heat capacity of γ-Fe2SiO4 between 5 and 303 K and derived thermodynamic properties     

Wenjun Yong  E. Dachs  A. C. Withers  E. J. Essene 《Physics and Chemistry of Minerals》2007,34(2):121-127

A multi-anvil device was used to synthesize 24 mg of pure γ-Fe₂SiO₄ crystals at 8.5 GPa and 1,273 K. The low-temperature heat capacity (C _p) of γ-Fe₂SiO₄ was measured between 5 and 303 K using the heat capacity option of a physical properties measurement system. The measured heat capacity data show a broad λ-transition at 11.8 K. The difference in the C _p between fayalite and γ-Fe₂SiO₄ is reduced as the temperature increases in the range of 50–300 K. The gap in C _p data between 300 and 350 K of γ-Fe₂SiO₄ is an impediment to calculation of a precise C _p equation above 298 K that can be used for phase equilibrium calculations at high temperatures and high pressures. The C _p and entropy of γ-Fe₂SiO₄ at standard temperature and pressure (S°₂₉₈) are 131.1 ± 0.6 and 140.2 ± 0.4 J mol⁻¹ K⁻¹, respectively. The Gibbs free energy at standard pressure and temperature (ΔG° _f,298) is calculated to be −1,369.3 ± 2.7 J mol⁻¹ based on the new entropy data. The phase boundary for the fayalite–γ-Fe₂SiO₄ transition at 298 K based on current thermodynamic data is located at 2.4 ± 0.6 GPa with a slope of 25.4 bars/K, consistent with extrapolated results of previous experimental studies.  相似文献   

Thermodynamic functions of eskolaite Cr<Subscript>2</Subscript>O<Subscript>3</Subscript>(c) at 0–1800 K     

V. M. Gurevich  O. L. Kuskov  N. N. Smirnova  K. S. Gavrichev  A. V. Markin 《Geochemistry International》2009,47(12):1170-1179

The heat capacity of eskolaite Cr₂O₃(c) was determined by adiabatic vacuum calorimetry at 11.99–355.83 K and by differential calorimetry at 320–480 K. Experimental data of the authors and data compiled from the literature were applied to calculate the heat capacity, entropy, and the enthalpy change of Cr₂O₃ within the temperature range of 0–1800 K. These functions have the following values at 298.15 K: C _p ⁰ (298.15) = 121.5 ± 0.2 J K⁻¹mol⁻¹, S ⁰(298.15) = 80.95 ± 0.14 J K⁻¹mol⁻¹, and H ⁰(298.15)-H ⁰(0) = 15.30±0.02 kJ mol⁻¹. Data were obtained on the transitions from the antiferromagnetic to paramagnetic states at 228–457 K; it was determined that this transition has the following parameters: Neel temperature T _N = 307 K, Δ _tr S = 6.11 ± 0.12 J K⁻¹mol⁻¹ and δ _tr H = 1.87 ± 0.04 kJ mol⁻¹.  相似文献   

Excess heat capacity and entropy of mixing along the chlorapatite–fluorapatite binary join     

Edgar Dachs  Daniel Harlov  Artur Benisek 《Physics and Chemistry of Minerals》2010,37(9):665-676

The heat capacity at constant pressure, C _p, of chlorapatite [Ca₅(PO₄)₃Cl – ClAp], and fluorapatite [Ca₅(PO₄)₃F – FAp], as well as of 12 compositions along the chlorapatite–fluorapatite join have been measured using relaxation calorimetry [heat capacity option of the physical properties measurement system (PPMS)] and differential scanning calorimetry (DSC) in the temperature range 5–764 K. The chlor-fluorapatites were synthesized at 1,375–1,220°C from Ca₃(PO₄)₂ using the CaF₂–CaCl₂ flux method. Most of the chlor-fluorapatite compositions could be measured directly as single crystals using the PPMS such that they were attached to the sample platform of the calorimeter by a crystal face. However, the crystals were too small for the crystal face to be polished. In such cases, where the sample coupling was not optimal, an empirical procedure was developed to smoothly connect the PPMS to the DSC heat capacities around ambient T. The heat capacity of the end-members above 298 K can be represented by the polynomials: C _p^ClAp = 613.21 − 2,313.90T ^−0.5 − 1.87964 × 10⁷ T ⁻² + 2.79925 × 10⁹ T ⁻³ and C _p^FAp = 681.24 − 4,621.73 × T ^−0.5 − 6.38134 × 10⁶ T ⁻² + 7.38088 × 10⁸ T ⁻³ (units, J mol⁻¹ K⁻¹). Their standard third-law entropy, derived from the low-temperature heat capacity measurements, is S° = 400.6 ± 1.6 J mol⁻¹ K⁻¹ for chlorapatite and S° = 383.2 ± 1.5 J mol⁻¹ K⁻¹ for fluorapatite. Positive excess heat capacities of mixing, ΔC _p^ex, occur in the chlorapatite–fluorapatite solid solution around 80 K (and to a lesser degree at 200 K) and are asymmetrically distributed over the join reaching a maximum of 1.3 ± 0.3 J mol⁻¹ K⁻¹ for F-rich compositions. They are significant at these conditions exceeding the 2σ-uncertainty of the data. The excess entropy of mixing, ΔS ^ex, at 298 K reaches positive values of 3–4 J mol⁻¹ K⁻¹ in the F-rich portion of the binary, is, however, not significantly different from zero across the join within its 2σ-uncertainty.  相似文献   

The low-pressure stability of phase A,Mg7Si2O8(OH)6     

A. R. Pawley  Bernard J. Wood 《Contributions to Mineralogy and Petrology》1996,124(1):90-97

 Phase A, Mg₇Si₂O₈(OH)₆, is a dense hydrous magnesium silicate whose importance as a host of H₂O in the Earth’s mantle is a subject of debate. We have investigated the low-pressure stability of phase A in experiments on the reaction phase A=brucite+forsterite. Experiments were conducted in piston-cylinder and multi-anvil apparatus, using mixtures of synthetic phase A, brucite and forsterite. The reaction was bracketed between 2.60 and 2.75 GPa at 500° C, between 3.25 and 3.48 GPa at 600° C and between 3.75 and 3.95 GPa at 650^° C. These pressures are much lower than observed in the synthesis experiments of Yamamoto and Akimoto (1977). At 750^° C the stability field of brucite + chondrodite was entered. The enthalpy of formation and entropy of phase A at 1 bar (10⁵ Pa), 298 K, were derived from the experimental brackets on the reaction phase A=brucite+forsterite using a modified version of the thermodynamic dataset THERMOCALC of Holland and Powell (1990), which includes a new equation of state of H₂O derived from the molecular dynamics simulations of Brodholt and Wood (1993). The data for phase A are: ΔH ^o _f =−7126±8 kJ mol^-1, S ^o=351 J K^-1 mol^-1. Incorporating these data into THERMOCALC allows the positions of other reactions involving phase A to be calculated, for example the reaction phase A + enstatite=forsterite+vapour, which limits the stability of phase A in equilibrium with enstatite. The calculated position of this reaction (753° C at 7 GPa to 937° C at 10 GPa) is in excellent agreement with the experimental brackets of Luth (1995) between 7 and 10 GPa, supporting the choice of equation of state of H₂O used in THERMOCALC. Comparison of our results with calculated P-T paths of subducting slabs (Peacock et al. 1994) suggests that, in the system MgO–SiO₂–H₂O, phase A could crystallise in compositions with Mg/Si>2 at pressures as low as 3 GPa. In less Mg rich compositions phase A could crystallise at pressures above approximately 6 GPa. Received: 3 July 1995/Accepted: 14 December 1995  相似文献   

Thermal and redox state of the subcontinental lithospheric mantle of NE Spain from thermobarometric data on mantle xenoliths     

Gumer Galán  V. Oliveras  B. A. Paterson 《International Journal of Earth Sciences》2011,100(1):81-106

Mantle xenoliths in within-plate Cenozoic alkaline mafic lavas from NE Spain are used to assess the local subcontinental lithospheric mantle geotherm and the influence of melting and metasomatism on its oxidation state. The xenoliths are mainly anhydrous spinel lherzolites and harzburgites and gradations between, with minor pyroxenites. Most types show protogranular textures, but transitional protogranular–porphyroclastic and equigranular lherzolites also exist. Different thermometers used in the estimates provide higher subsolidus equilibrium temperatures for harzburgites (1,062 ± 29°C) than for lherzolites (972 ± 89°C), although there is overlap; the lowest temperatures correspond to porphyroclastic lherzolites, whereas pyroxenites give the highest temperatures (up to 1,257°C). Maximum pressures for subsolidus equilibrium of peridotites are at 2.0–1.8 GPa. Later they followed adiabatic decompression and harzburgites registered lower pressures (1.02 ± 0.19 GPa) than lherzolites (1.41 ± 0.27 GPa). One pyroxenite gives values consistent with the spinel lherzolite field (1.08 GPa). The shallowest barometric data are in agreement with the highest local conductive geotherms, which implies that the lithosphere–asthenosphere boundary is at 70–60 km minimum depth. Higher equilibrium temperatures for the harzburgites could be explained by the existence of mafic magma bodies or dykes at the lower crust–mantle boundary. Paleo-fO₂ conditions during partial melting as inferred from the covariation between V and MgO concentrations are mainly between QFM−1 and QFM−2 in log units. However, most thermobarometric fO₂ estimates are between QFM−1 and QFM+1, suggesting oxidation caused by later metasomatism during uplift and cooling.  相似文献   

Low-temperature thermodynamic properties of disordered zeolites of the natrolite group     

I. E. Paukov  N. K. Moroz  Yu. A. Kovalevskaya  I. A. Belitsky 《Physics and Chemistry of Minerals》2002,29(4):300-306

 The heat capacity of paranatrolite and tetranatrolite with a disordered distribution of Al and Si atoms has been measured in the temperature range of 6–309 K using the adiabatic calorimetry technique. The composition of the samples is represented with the formula (Na_1.90K_0.22Ca_0.06)[Al_2.24Si_2.76O₁₀]·nH₂O, where n=3.10 for paranatrolite and n=2.31 for tetranatrolite. For both zeolites, thermodynamic functions (vibrational entropy, enthalpy, and free energy function) have been calculated. At T=298.15 K, the values of the heat capacity and entropy are 425.1 ± 0.8 and 419.1 ±0.8 J K⁻¹ mol⁻¹ for paranatrolite and 381.0 ± 0.7 and 383.2 ± 0.7 J K⁻¹ mol⁻¹ for tetranatrolite. Thermodynamic functions for tetranatrolite and paranatrolite with compositions corrected for the amount of extraframework cations and water molecules have also been calculated. The calculation for tetranatrolite with two water molecules and two extraframework cations per formula yields: C _p (298.15)=359.1 J K⁻¹ mol⁻¹, S(298.15) −S(0)=362.8 J K⁻¹ mol⁻¹. Comparing these values with the literature data for the (Al,Si)-ordered natrolite, we can conclude that the order in tetrahedral atoms does not affect the heat capacity. The analysis of derivatives dC/dT for natrolite, paranatrolite, and tetranatrolite has indicated that the water- cations subsystem within the highly hydrated zeolite may become unstable at temperatures above 200 K. Received: 30 July 2001 / Accepted: 15 November 2001  相似文献   

Equation of state, elasticity, and shear strength of pyrite under high pressure   总被引：1，自引：1，他引：1  

S. Merkel  A. P. Jephcoat  J. Shu  H.-K. Mao  P. Gillet  R. J. Hemley 《Physics and Chemistry of Minerals》2002,29(1):1-9

 Physical properties including the equation of state, elasticity, and shear strength of pyrite have been measured by a series of X-ray diffraction in diamond-anvil cells at pressures up to 50 GPa. A Birch–Murnaghan equation of state fit to the quasihydrostatic pressure–volume data obtained from laboratory X-ray source/film techniques yields a quasihydrostatic bulk modulus K _0T =133.5 (±5.2) GPa and bulk modulus first pressure derivative K ^′ _0T =5.73 (±0.58). The apparent equation of state is found to be strongly dependent on the stress conditions in the sample. The stress dependency of the high-pressure properties is examined with anisotropic elasticity theory from subsequent measurements of energy-dispersive radial diffraction experiments in the diamond-anvil cell. The calculated values of K _0T depend largely upon the angle ψ between the diffracting plane normal and the maximum stress axis. The uniaxial stress component in the sample, t=σ₃−σ₁, varies with pressure as t=−3.11+0.43P between 10 and 30 GPa. The pressure derivatives of the elastic moduli dC ₁₁/dP=5.76 (±0.15), dC ₁₂/dP=1.41 (±0.11) and dC ₄₄/dP=1.92 (±0.06) are obtained from the diffraction data assuming previously reported zero-pressure ultrasonic data (C ₁₁=382 GPa, C ₁₂=31 GPa, and C ₄₄=109 GPa). Received: 21 December 2000 / Accepted: 11 July 2001  相似文献   

Thermoelastic properties of the high-pressure phase of SnO2 determined by in situ X-ray observations up to 30 GPa and 1400 K     

S. Ono  E. Ito  T. Katsura  A. Yoneda  M. J. Walter  S. Urakawa  W. Utsumi  K. Funakoshi 《Physics and Chemistry of Minerals》2000,27(9):618-622

 In situ synchrotron X-ray experiments in the system SnO₂ were made at pressures of 4–29 GPa and temperatures of 300–1400 K using sintered diamond anvils in a 6–8 type high-pressure apparatus. Orthorhombic phase (α-PbO₂ structure) underwent a transition to a cubic phase (Pa3ˉ structure) at 18 GPa. This transition was observed at significantly lower pressures in DAC experiments. We obtained the isothermal bulk modulus of cubic phase K ₀= 252(28) GPa and its pressure derivative K ^′=3.5(2.2). The thermal expansion coefficient of cubic phase at 25 GPa up to 1300 K was determined from interpolation of the P-V-T data obtained, and is 1.7(±0.7) × 10⁻⁵ K⁻¹ at 25 GPa. Received: 7 December 1999 / Accepted: 27 April 2000  相似文献   

Heat capacity and phase equilibria of wadeite-type K2Si4O9     

Wenjun Yong  E. Dachs  A. C. Withers  E. J. Essene 《Contributions to Mineralogy and Petrology》2008,155(2):137-146

The low-temperature heat capacity (C _p) of Si-wadeite (K₂Si₄O₉) synthesized with a piston cylinder device was measured over the range of 5–303 K using the heat capacity option of a physical properties measurement system. The entropy of Si-wadeite at standard temperature and pressure calculated from the measured heat capacity data is 253.8 ± 0.6 J mol⁻¹ K⁻¹, which is considerably larger than some of the previous estimated values. The calculated phase transition boundaries in the system K₂O–Al₂O₃–SiO₂ are generally consistent with previous experimental results. Together with our calculated phase boundaries, seven multi-anvil experiments at 1,400 K and 6.0–7.7 GPa suggest that no equilibrium stability field of kalsilite + coesite intervenes between the stability field of sanidine and that of coesite + kyanite + Si-wadeite, in contrast to previous predictions. First-order approximations were undertaken to calculate the phase diagram in the system K₂Si₄O₉ at lower pressure and temperature. Large discrepancies were shown between the calculated diagram compared with previously published versions, suggesting that further experimental or/and calorimetric work is needed to better constrain the low-pressure phase relations of the K₂Si₄O₉ polymorphs. Electronic supplementary material The online version of this article (doi:) contains supplementary material, which is available to authorized users.  相似文献   

Thermodynamic data of the high-pressure phase Mg5Al5Si6O21(OH)7 (Mg-sursassite)     

K.-D. Grevel  A. Navrotsky  W. A. Kahl  D. W. Fasshauer  J. Majzlan 《Physics and Chemistry of Minerals》2001,28(7):475-487

 Calorimetric and P–V–T data for the high-pressure phase Mg₅Al₅Si₆O₂₁(OH)₇ (Mg-sursassite) have been obtained. The enthalpy of drop solution of three different samples was measured by high-temperature oxide melt calorimetry in two laboratories (UC Davis, California, and Ruhr University Bochum, Germany) using lead borate (2PbO·B₂O₃) at T=700 ^∘C as solvent. The resulting values were used to calculate the enthalpy of formation from different thermodynamic datasets; they range from −221.1 to −259.4 kJ mol⁻¹ (formation from the oxides) respectively −13892.2 to −13927.9 kJ mol⁻¹ (formation from the elements). The heat capacity of Mg₅Al₅Si₆O₂₁(OH)₇ has been measured from T=50 ^∘C to T=500 ^∘C by differential scanning calorimetry in step-scanning mode. A Berman and Brown (1985)-type four-term equation represents the heat capacity over the entire temperature range to within the experimental uncertainty: C _P (Mg-sursassite) =(1571.104 −10560.89×T ^−0.5−26217890.0 ×T ⁻²+1798861000.0×T ⁻³) J K⁻¹ mol⁻¹ (T in K). The P V T behaviour of Mg-sursassite has been determined under high pressures and high temperatures up to 8 GPa and 800 ^∘C using a MAX 80 cubic anvil high-pressure apparatus. The samples were mixed with Vaseline to ensure hydrostatic pressure-transmitting conditions, NaCl served as an internal standard for pressure calibration. By fitting a Birch-Murnaghan EOS to the data, the bulk modulus was determined as 116.0±1.3 GPa, (K ^′=4), V _T,0 =446.49 ³ exp[∫(0.33±0.05) × 10⁻⁴ + (0.65±0.85)×10⁻⁸ T dT], (K _T/T) _P  = −0.011± 0.004 GPa K⁻¹. The thermodynamic data obtained for Mg-sursassite are consistent with phase equilibrium data reported recently (Fockenberg 1998); the best agreement was obtained with Δ_f H ⁰ ₂₉₈ (Mg-sursassite) = −13901.33 kJ mol⁻¹, and S ⁰ ₂₉₈ (Mg-sursassite) = 614.61 J K⁻¹ mol⁻¹. Received: 21 September 2000 / Accepted: 26 February 2001  相似文献