| STUDY ON THE CORROSION PEAK OF CARBON STEEL IN MARINE SPLASH ZONE |
| |
| 作者姓名： | 朱相荣 黄桂桥 梁采凤 |
| |
| 摘 要： | lNTRODUCTI0NSincetheoonceptofrnarinesplashzone(MSZ)wasfirstproposedbyHumble,rnanyresearchesprovedthatthecorrosionofsteelinthesplashzoneisthemostseriousinthemarineenvironninetandthatthisMSZcorrosionhasapeak(Zhu,l995).Howevertheenvironmentalfactorscatisingthecorrosionpeakwasnotkn0wnthen(Niat0,l975,Atsushi,l994)andtherangeoftheMSZwasnotyetdeariydefinedopzkaki,l985).ThispaperexplainsthemaincauseofthecormsionpeakanddefinestheexaCtrangeoftheMSZinsomeofChina'sharbours.MATERIALSANDMET…
|
| 收稿时间： | 18 March 1996 |
| 修稿时间： | 21 January 1997 |
Study on the corrosion peak of carbon steel in marine splash zone |
| |
| Zhu Xiang-rong,Huang Gui-qiao,Liang Cai-feng.STUDY ON THE CORROSION PEAK OF CARBON STEEL IN MARINE SPLASH ZONE[J].Chinese Journal of Oceanology and Limnology,1997,15(4):378-380. |
| |
| Authors: | Zhu Xiang-rong Huang Gui-qiao Liang Cai-feng |
| |
| Institution: | (1) Central Iron & Steel Research Institute, Qingdao Research Institute for Marine Corrosion, 266071 Qingdao |
| |
| Abstract: | This study determined that the range of the marine splash zone (MSZ) of China's Qingdao,Zhoushan. Xiamen. Zhanjiang harbour area was about 0-2.4 m above the mean high water level (MHWL) of the seawater that the MSZ corrosion peak (MSZCP) was usually 0.6- 1.2 m above the MHWL. and was caused by the large salt particle accumulation on the A3 carbon steel test sample surface and by the high frequency altemations of wet and dry environmental conditions around the samples. |
| |
| Keywords: | carbon steel marine splash zone corrosion peak |