| ELECTROCHEMICAL CORROSION BEHAVIOR OF STEEL IN THE JUNCTURE AREA OF SEA CLAY AND SAND |
| |
| 作者姓名： | 张经磊 侯保荣 郭公玉 杨芳英 谢肖勃 |
| |
| 作者单位： | Institute of Oceanology，Academa Sinica，Qingdao 266071，Institute of Oceanology，Academa Sinica，Qingdao 266071，Institute of Oceanology，Academa Sinica，Qingdao 266071，Institute of Oceanology，Academa Sinica，Qingdao 266071，Institute of Oceanology，Academa Sinica，Qingdao 266071 |
| |
| 基金项目： | This work was supported by Corrosion Science Laboratory，Institute of Corrosion and Protection of Mctals, Academia Sinica |
| |
| 摘 要： | Corrosion behavior of steel in the juncture area of sea clay and sand was studied. The results show that galvanic corrosion occurred between steel samples buried in sea clay and sand, and that the polarity of the galvanic cell reversed after some testing later. The cause of reversing of polarity is discussed.
|
| 收稿时间： | 26 August 1992 |
Electrochemical corrosion behavior of steel in the juncture area of sea clay and sand |
| |
| Zhang Jinglei,Hou Baorong,Guo Gongyu,Yang Fangying,Xie Xiaobo.ELECTROCHEMICAL CORROSION BEHAVIOR OF STEEL IN THE JUNCTURE AREA OF SEA CLAY AND SAND[J].Chinese Journal of Oceanology and Limnology,1993,11(2):171-175. |
| |
| Authors: | Zhang Jinglei Hou Baorong Guo Gongyu Yang Fangying Xie Xiaobo |
| |
| Institution: | (1) Institute of Oceanology, Academia Sinica, 266071 Qingdao |
| |
| Abstract: | Corrosion behavior of steel in the juncture area of sea clay and sand was studied. The results show that galvanic corrosion occurred between steel samples buried in sea clay and sand, and that the polarity of the galvanic cell reversed after some testing later. The cause of reversing of polarity is discussed. |
| |
| Keywords: | corrosion sted juncture area clay sand |