Dewatering Behaviour of a Uranium Ore Slurry Containing Clays |
| |
| Authors: | Maki Ito Shahid Azam |
| |
| Institution: | 1.Environmental Systems Engineering, Faculty of Engineering and Applied Science,University of Regina,Regina,Canada |
| |
| Abstract: | The main objective of this paper was to investigate the dewatering behaviour of a clayey uranium ore slurry. The slurry (containing 28% clay size) exhibited moderate water adsorption (w l = 83% and w p = 30%). Primarily composed of muscovite (46%) and quartz (30%), the clay minerals included illite (8%), chlorite (5%) and kaolinite (2%) alongside a CEC of 41 (cmol(+)/kg) with Ca2+ and Mg2+ as the dominant cations. Likewise, the high EC (17,600 μS/cm) and ionic strength (1.15 mol/L) indicated a flocculated microstructure due to the presence of SO4 2? (22,600 mg/L) and Mg2+ (1340 mg/L) in the slurry water. Settling included sedimentation and consolidation at low initial solids condition (25–35%) whereas only consolidation was observed at high initial solids contents (40–50%). The average k reduced from 1.2 × 10?6 m/s (initial s = 25%) to 5.3 × 10?8 m/s (initial s = 50%) along with a void ratio reduction from 7.4 to 2.6. Due to thixotropic strength, volume compressibility during consolidation showed apparent pre-consolidation at low effective stress (0.3–2 kPa) with a reduction in void ratio from 2.6 to 2.5. The e s was found to be 2.46 at σ′ = 2 kPa and was followed by a steeper slope with the void ratio reducing to 2.1 at σ′ = 31 kPa. Likewise, the hydraulic conductivity during consolidation decreased from 2.6 × 10?9 m/s (at e = 2.6) to 2.0 × 10?10 m/s (at e = 2.1). |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|