Deferrization of Potassium-Rich Rocks And Hydrothermal Decomposition Using KOH |
| |
| Institution: | ;1.School of materials science and technology;2.China University of Geosciences |
| |
| Abstract: | The potassium-feldspar can be decomposed using the KOH as additive via hydrothermal synthesis methods, which can destroy the structure of the potassium-feldspar and turns its K+ into water soluble potash resources and make its silica component utilized. The potassium-feldspar from Inner Mogolia was decomposed after iron removing and hydrothermal processes successively. The results showed(Table 1) that the iron could be removed up to 98.56% after the treatment of 90℃ for 2 hours with 5.8mol/L density of HCL solution. It is seen from the Table 1that the content of iron significantly decreased while the content of SiO2, Al2O3, K2O increase. The treated sample was used to be decomposed by hydrothermal method in KOH solution. The results showed that the dissolution rate of SiO2 could be up to 64.73% after the hydrothermal treatment of 260 ℃ for 2 hours with 1.2 mol/L density of KOH(Fig 1). The solid product is mailnly kalsilite phase. |
| |
| Keywords: | |
|
|