The effect of iron on montmorillonite stability. (II) Experimental investigation |
|
| Authors: | James Wilson Gordon Cressey Javier Cuadros David Savage |
| Institution: | a Chemical Hazards and Poisons Division (London), Health Protection Agency, Medical Toxicology Unit, Avonley Road, London SE14 5ER, UK b Department of Earth Sciences, University of Bristol, Wills Memorial Building, Queen’s Road, Bristol, BS8 1RJ, UK c Department of Mineralogy, The Natural History Museum, Cromwell Road, London SW7 5BD, UK d School of Chemistry, University of Southampton, SO17 1BJ, UK e Quintessa Ltd. 24 Trevor Road, West Bridgford, Nottingham NG2 6FS, UK f Japan Nuclear Cycle Development Institute, Tokai-mura Prefecture, Japan |
| Abstract: | Several designs proposed for high-level nuclear waste (HLW) repositories include steel waste canisters surrounded by montmorillonite clay. This work investigates montmorillonite stability in the presence of native Fe, magnetite and aqueous solutions under hydrothermal conditions. Two series of experiments were conducted. In the first, mixtures of Na-montmorillonite, magnetite, native Fe, calcite, and NaCl solutions were reacted at 250 °C, Psat for between 93 and 114 days. In the second series, the starting mixtures included Na-montmorillonite, native Fe and solutions of FeCl2 which were reacted at temperatures of 80, 150, and 250 °C, Psat, for 90-92 days. Experiments were analysed using XRD, FT-IR, TEM, ICP-AES, and ICP-MS. In the first series of experiments, native Fe oxidised to produce magnetite and the starting montmorillonite material was transformed to Fe-rich smectite only when the Fe was added predominantly as Fe metal rather than Fe oxide (magnetite). The Fe-rich smectite was initially Fe(II)-rich, which oxidised to produce an Fe(III)-rich form on exposure to air. The expansion of this material on ethylene glycol solvation was much reduced compared to the montmorillonite starting material. TEM imaging shows that partial loss of tetrahedral sheets occurred during transformation of the montmorillonite, resulting in adjacent layers becoming H-bonded with a 7 Å repeat. The reduced swelling property of the Fe-smectite product may be due predominantly to the structural disruption of smectite layers and the formation of H-bonds. Solute activities corresponded to the approximate stability field calculated for hypothetical Fe(II)-saponite. In the second series of experiments, significant smectite alteration was only observed at 250 °C and the product contained a small proportion of a 7 Å repeat structure, observable by XRD. In these experiments, solute activities coincide with berthierine. The experiments indicate that although bentonite is still a desirable choice of backfill material for HLW repositories, some loss of expandability may result if montmorillonite is altered to Fe-rich smectite at the interface between steel canisters and bentonite. |
| Keywords: | |
| 本文献已被 ScienceDirect 等数据库收录！ | |