Refinement of the crystal structure of papagoite,CaCuAlSi2O6(OH)3 |
| |
| Authors: | Dr L A Groat Dr F C Hawthorne |
| |
| Institution: | (1) Department of Geological Sciences, University of Manitoba, R3T 2N2 Winnipeg, Manitoba, Canada |
| |
| Abstract: | Summary The crystal structure of papagoite, CaCuAlSi2O6(OH)3, monoclinic,a = 2.926 (3),b = 11.496 (3),c = 4.696 (1) Å,  = 100.81 (2)°, V = 685.4 (3) Å3, space groupC 2/m,Z = 4, has been refined to anR index of 3.4% for 913 observed reflections measured with MoK X-radiation. The single unique Cu cation is surrounded by six anions in a pseudo-octahedral arrangement showing strong Jahn-Teller distortion. Edge-sharing  rutile-like chains of pseudo-octahedrally coordinated Cu and Al extend in the Y direction, and are cross-linked into an octahedral sheet by Ca2Ø10 (O = unspecified ligand, O or OH) dimers. These sheets are linked by (Si4O12) rings to form a mixed tetrahedral-octahedral framework.
Verfeinerung der Kristallstruktur von Papagoit, CaCuAlSi2O6(OH)3
Zusammenfassung Die Kristallstruktur von Papagoit, CaCuAlSi2O6(OH)3, monoklina = 12,926 (3),b = 11.496 (3),c = 4.696 (1) Å, = 100.81 (2)°,V = 685.4 (3) Å3, RaumgruppeC2/m,Z = 4, wurde für 913 beobachtete, MoK-Röntgenstrahlung gemessene Reflexe aufR = 3,4% verfeinert. Das eine symmetrieunabhängige Kupfer-Kation ist pseudooktaedrisch von sechs Anionen mit einer starken Jahn-Teller-Verzerrung umgeben. Die pseudo-oktaedrisch koordinierten Cu- und Al-Atome werden über Kanten zu parallel zur y-Achse verlaufenden  rutil-ähnlichen Ketten verbunden, die zusammen mit den Ca2Ø10-Gruppen (Ø = nicht spezifsierter Ligand, O bzw. OH) Oktaederschichten bilden. Diese Schichten werden durch (Si4O12)-Ringe zu einem aus Tetraedern und Oktaedern bestehenden Netzwerk verknüpft.
With 4 Figures |
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|