| 热压碳化钨基复合胎体材料性能试验 | |
| 引用本文： | 马银龙,孙友宏,高科,刘宝昌,张献振,李小洋.热压碳化钨基复合胎体材料性能试验[J].吉林大学学报(地球科学版),2013,43(1):207-211. |
| 作者姓名： | 马银龙 孙友宏 高科 刘宝昌 张献振 李小洋 |
| 作者单位： | 1.吉林大学建设工程学院，长春130026; 2.吉林大学超硬材料国家重点实验室，长春130012; 3.中煤科工集团西安研究院，西安710077 |
| 基金项目： | 国土资源部公益性行业科研专项项目(SinoProbe-09-05);国家“863”计划项目(2009AA06Z201);国家自然科学基金青年基金项目(51004052) |
| 摘 要： | 为了提高碳化钨（WC）基复合胎体材料的性能，在烧结压力为13 MPa、升温时间为6 min、保温时间为5 min的情况下，采用真空热压烧结的方法制备了金刚石钻头所用的10种不同比例WC基胎体材料试样30块，并对试样进行了洛氏硬度(HRC)、抗弯强度(σ)等性能测试。通过试验数据分析研究了WC、663青铜(ZQSn663)、锰(Mn)、钴(Co)、镍(Ni)与胎体材料HRC和σ的关系。结果表明：WC质量分数对胎体的HRC和σ的影响是主要因素，胎体的HRC和σ具有内在联系，HRC高的胎体σ往往也高；在胎体配方中各个成分的含量都应得到控制才能保证胎体的性能优良，各成分的质量分数控制为：w(WC)<59.1%, w(ZQSn663)>25%, 3%<w(Ni)<6.5%, 0.9%<w(Co)<3.5%, w(WC-ZQSn663)<20%。 |
| 关 键 词： | 碳化钨基复合材料 金刚石钻头 热压烧结 |
| 收稿时间： | 2012-04-29 |
Experiment on WC Matrix Composites Performance Prepared by Hot-Pressing Sintering |
|
| Ma Yinlong,Sun Youhong,Gao Ke,Liu Baochang,Zhang Xianzhen,Li Xiaoyang.Experiment on WC Matrix Composites Performance Prepared by Hot-Pressing Sintering[J].Journal of Jilin Unviersity:Earth Science Edition,2013,43(1):207-211. | |
| Authors: | Ma Yinlong Sun Youhong Gao Ke Liu Baochang Zhang Xianzhen Li Xiaoyang |
| Institution: | 1.College of Construction Engineering，Jilin University，Changchun130026, China; 2.State Key Lab Superhard Mat, Jilin University,Changchun130012, China; 3.Xi’an Research Institute, China Coal Technology Engineering Group, Xi’an710077, China |
| Abstract: | For getting better properties of WC matrix composites, the performance such as the rockwell hardness and bending strength, etc. of 30 WC matrix composites, prepared by 10 different formulas, are tested. These samples were manufactured by the vacuum hot-pressing sintering process using intermediate-frequency furnace under the conditions that sintering pressure is 13 MPa, the heating time is 6 min, and the holding time is 5 min. The influence of WC, copper ZQSn663, Mn, Co, and Ni on the hardness and bending strength properties of matrix are investigated by data analysis. The results indicate that WC is the prime factor to influence the hardness and bending strength of matrix. Internal logic exists between the hardness of matrix and bending strength. The matrix with high hardness has high strength, too. To get excellent performance of the matrix, the proportion of elements by weight should be controlled in formula: WC<59.1%, ZQSn663>25%,3% |
| Keywords: | WC matrix composites diamond drills hot-pressed sintering |
| 本文献已被 CNKI 等数据库收录！ | |
| 点击此处可从《吉林大学学报(地球科学版)》浏览原始摘要信息 | |
| 点击此处可从《吉林大学学报(地球科学版)》下载免费的PDF全文 | |