An experimental study of the formation of metallic iron in chondrules |
| |
| Authors: | Bosmat A Cohen Roger H Hewins |
| |
| Institution: | 1 Geological Sciences, Rutgers University, 610 Taylor Road, Piscataway, NJ 08854, USA |
| |
| Abstract: | The abundance of metallic iron is highly variable in different kinds of chondrites. The precise mechanism by which metal fractionation occurred and its place in time relative to chondrule formation are unknown. As metallic iron is abundant in most Type I (FeO-poor) chondrules, determining under what conditions metal could form in chondrules is of great interest. Assuming chondrules were formed from low temperature nebular condensate, we heated an anhydrous CI-like material at 1580°C in conditions similar to those of the canonical nebula (PH2 = 1.3 × 10−5 atm). We reproduced many of the characteristics of Type IA and IIA chondrules but none of them contained any iron metal. In these experiments FeO was abundant in charges that were heated for as long as 6 h. At a lower temperature, 1350°C, dendritic/cellular metal crystallized from Fe-FeS melts during the evaporation of S. However, the silicate portion consisted of many relict grains and vesicles, not typical of chondrules.Evaporation experiments conducted at PH2 = 1 atm and 1565°C produced charges containing metallic iron both as melt droplets and inclusions in olivine, similar to those found in chondrules. Formation of iron in these experiments was primarily the result of desulfurization of FeS. With long heating times Fe° was lost by evaporation. Apart from some reduction of FeO by kerogen to make metal inclusions within olivine grains, reduction of FeO to make Fe° in these charges was not observed.This study shows that under canonical nebular conditions FeS and iron-metal are extremely volatile so that metal-rich Type I chondrules could not form by melting “CI.” Under these conditions FeO is lost predominantly by hydrogen stripping and, due to the relative low abundance of hydrogen at low pressures, remains in the melt for as long as 6 h. Conversely, at higher total pressures (1-atm H2) iron metal (produced mainly by the desulfurization of troilite) is less volatile and remains in the melt for longer times (at least 6 h). In addition, due to elevated pressures of hydrogen, FeO is stripped away much faster. These results suggest that chondrule formation occurred in environments with elevated pressures relative to the canonical nebula for iron metal to be present. |
| |
| Keywords: | |
| 本文献已被 ScienceDirect 等数据库收录！ |
|