Stress-induced crack path in Aji granite under tensile stress |
| |
| Authors: | Yozo Kudo Osam Sano Naokuni Murashige Yoshiaki Mizuta Koji Nakagawa |
| |
| Institution: | (1) Tokuyama College of Technology, 745 Tokuyama, Japan;(2) Yamaguchi University, 755 Ube, Japan |
| |
| Abstract: | The double-torsion test using Aji granite was carried out to investigate the interaction between stress-induced crack path and mineral grains. Crack velocities were controlled at range 10–7 m/s to 10–1 m/s. After the stressed specimens were dyed, we checked the crack path by thin section analysis, using an optical microscope. The stress-induced crack path was divided into two types, transgranular and intergranular cracks, and each path was subdivided with respect to mineral grains. In spite of the extensive range of crack velocities, the ratios between the transgranular and intergranular crack lengths did not change. The crack paths were all jagged, and often showed detour around the grain boundary when faced with obstacles like hard grains or preexisting cracks. That is to say, quartz grain played an important role as an obstacle. Feldspar grain could change the crack path because of its cleavage plane. Biolite grain had a serious effect on the path even if its constitution ratio is very small. Fractal dimensions of the crack paths were calculated by three methods, as indicators of surface roughness. The fractal dimensions were shown in a slight trend with the change of crack velocity. This trend can be explained from the point of limited cracking rate in stress corrosion. |
| |
| Keywords: | Stress-induced crack granite tensile strength fractal double-torsion test stress corrosion |
| 本文献已被 SpringerLink 等数据库收录！ |
|