| 海水为溶剂合成纳米粉煤灰沸石及其性能表征 |
| |
| 引用本文： | 于艳卿,邹晓兰,李超峰,朱校斌.海水为溶剂合成纳米粉煤灰沸石及其性能表征[J].海洋科学,2012,36(1):49-53. |
| |
| 作者姓名： | 于艳卿 邹晓兰 李超峰 朱校斌 |
| |
| 作者单位： | 1. 中国科学院海洋研究所,山东青岛266071／中国科学院研究生院,北京100049
2. 中国科学院海洋研究所,山东青岛,266071 |
| |
| 基金项目： | 国家十一五科技支撑计划项目(2006BAB03A12); 国家863 计划项目(2006AA06Z362); 国家自然科学基金项目(30530080) |
| |
| 摘 要： | 以海水为溶剂,采用熔融法合成了纳米粉煤灰沸石。粉煤灰与NaOH的质量比为1:1.2,熔融温度550℃,熟料质量与海水固液的体积比为1:5(g/mL),晶化温度100℃,晶化时间6h。通过仪器分析和化学方法,对产物的结构、形貌、性能进行表征。同时,研究了产物的矿物组成、形貌、比表面积、阳离子交换量及化学组成。结果表明:产物为NaX型沸石和羟基方钠石的复合型沸石,海水晶化粉煤灰通过碱熔融法得到沸石质量优于传统水热法。合成沸石的性能和各项应用指标表明,所合成的沸石具有良好的实际应用价值。
|
| 关 键 词： | 粉煤灰 海水 熔融水热法 沸石 |
| 收稿时间： | 2010/12/25 0:00:00 |
| 修稿时间： | 2011/4/20 0:00:00 |
Synthesis and characterization of nano-fly ash zeolites made using seawater for crystallization |
| |
| YU Yan-qing,ZOU Xiao-lan,LI Chao-feng,ZHU Xiao-bin.Synthesis and characterization of nano-fly ash zeolites made using seawater for crystallization[J].Marine Sciences,2012,36(1):49-53. |
| |
| Authors: | YU Yan-qing ZOU Xiao-lan LI Chao-feng ZHU Xiao-bin |
| |
| Institution: | 1(1.Institute of Oceanology,the Chinese Academy of Sciences,Qingdao 266071,China;2.Graduate School of the Chinese Academy of Sciences,Beijing 100049,China) |
| |
| Abstract: | Nano-fly ash zeolites were synthesized using fusion method with seawater as solvent. The synthetic conditions were as follows: ash/NaOH quality ratio is 1:1.2, fusion temperature is 550°C, the mixture/seawater volume ratio is 1:5, reaction temperature is 100°C and reaction time is 6h. The structure, appearance and properties of the products were characterized and analyzed in detail with both instrumental and chemical analysis methods. In addition, the mineral composition, crystallization, surface area, capacity of the cation exchange, average particle size and chemical composition of synthesized zeolites were investigated and compared. The results showed that the product is a mixture of NaX zeolite and hydroxysodalite. This synthesized zeolite by fusion method using seawater for crystallization has higher purity and better crystallization than that by conventional hydrothermal method. The properties and characters of this synthesized zeolite show that it has good application values. |
| |
| Keywords: | coal fly ash seawater melting hydrothermal method zeolites |