| 利用提钾废渣和粉煤灰制备矿物聚合材料的实验研究 |
| |
| 引用本文： | 王刚,马鸿文,冯武威,丁秋霞.利用提钾废渣和粉煤灰制备矿物聚合材料的实验研究[J].岩石矿物学杂志,2003,22(4):453-457. |
| |
| 作者姓名： | 王刚 马鸿文 冯武威 丁秋霞 |
| |
| 作者单位： | 中国地质大学,材料科学与工程学院,北京,100083 |
| |
| 基金项目： | 教育部博士学科点基金资助项目 ( 19990 49114 )，内蒙古自治区科技攻关资助项目 ( 2 0 0 2 0 3 0 7) |
| |
| 摘 要： | 利用富钾岩石提钾后的废渣代替硅酸钠 (钾 )、大部分高岭石和氢氧化钠 (钾 ) ,以粉煤灰为主要原料 ,制备出矿物聚合材料 ,并采用正交实验确定其优化工艺条件为 :煅烧高岭石用量为 10 %～ 15 % ,废渣用量约 35 % ,氢氧化钠用量为 5 %～ 6 %。代表性样品的 7d抗压强度可达到 4 0～ 5 0MPa ,耐酸性、耐碱性分别为 99.99%和 10 0 % ,密度1.77～ 1.88g/cm3 ,收缩率 0 .13%～ 0 .2 8% ,导热系数 0 .4 8～ 0 .5 1W/m·K ,平均硬度 3.4 3。X射线粉末衍射分析表明 ,由铝硅酸盐聚合反应形成的基体相呈非晶态。扫描电镜分析絮凝状的基体相与粉煤灰玻璃体结合紧密 ,从而为制品具备良好的力学性能提供了结构基础。该矿物聚合材料成本低廉 ,同时又能利用粉煤灰等工业固体废物而达到改善环境的目的
|
| 关 键 词： | 富钾岩石 提钾废渣 粉煤灰 矿物聚合材料 力学性能 |
| 文章编号： | 1000-6524(2003)04-0453-05 |
| 修稿时间： | 2003年7月25日 |
The preparation of mineral polymer from potassium-distilled waste residue and fly ash: an experimental study |
| |
| WANG Gang,MA Hong_wen,FENG Wu_wei and DING Qiu_xia.The preparation of mineral polymer from potassium-distilled waste residue and fly ash: an experimental study[J].Acta Petrologica Et Mineralogica,2003,22(4):453-457. |
| |
| Authors: | WANG Gang MA Hong_wen FENG Wu_wei and DING Qiu_xia |
| |
| Abstract: | Fly ash was used as the main material to prepare mineral polymer in this study. The potassium_distilled waste residue obtained from potassium_rich slate was used as the raw material to replace sodium (potassium) silicate, calcined kaolin, sodium (potassium) hydroxide which are frequently used abroad to prepare mineral polymer. In this way, mineral polymer was prepared. The optimal technical parameters were determined by the orthogonal experiments: the weight proportions of calcined kaolin, waste residue and sodium hydroxide are about 10%~15%, 35% and 5%~6%, respectively. Compressive strengths of the representative mineral polymer samples were tested up to 40~50 MPa after 7d''s solidification. Tests show that the acid and alkali resistances of the samples are 99.99% and 100%, respectively, and their density, contractility, thermal conductivity and mean rigidity are 1.77~1.88
g/cm3, 0.13%~0.28%, 0.48~0.51 W/m·K and 3.43, respectively. XRD analysis shows that the matrix phase is amorphous.SEM photograph analysis shows that the floccule matrix phase is combined closely with the glass phase of the fly ash, which provides
a good structural basis for the samples. The cost of mineral polymer is low, and it can improve the environment by the utilization of
offal-like fly ash. |
| |
| Keywords: | potassium-rich rock potassium-distilled waste residue mineral polymer fly ash |