Synthesis of Pb-Feldspar by Ion Exchange Reaction and Its Implications |
| |
作者姓名: | LIU Rui LU Anhuai QIN Shan |
| |
作者单位: | [1]Land and Resources Department, Changchun Institute of Technology, Changchun, Jilin 130021 [2]School of Earth and Space Sciences, Peking University, Beijing 100871 |
| |
基金项目: | 国家重点基础研究发展计划(973计划) |
| |
摘 要: | Feldspar and Pb(NO3)2 were mixed and reacted at T=380℃ to synthesize Pb-feldspar. In the XRD (X-ray diffraction) pattern of the product, the d values (crystal lattice spacing) of the five peaks are 0.654, 0.342, 0.332, 0.327 and 0.257 nm. The XPS analysis results show that the binding energy of Pb 4f(7/2) in the feldspar was between 137.81-138.03 eV. Pb^2+ can replace alkali and alkali earth cations in the feldspar structure through ion exchange reaction to form Pb-feldspar.
|
关 键 词: | 离子交换 铅 长石 X射线衍射 多孔聚苯乙烯 结构合成 |
收稿时间: | 2006-01-11 |
修稿时间: | 2006-02-17 |
Synthesis of Pb-Feldspar by Ion Exchange Reaction and Its Implications |
| |
Authors: | LIU;Rui;LU;Anhuai;QIN;Shan |
| |
Abstract: | Abstract Feldspar and Pb(NO3)2 were mixed and reacted at T=380°C to synthesize Pb‐feldspar. In the XRD (X‐ray diffraction) pattern of the product, the d values (crystal lattice spacing) of the five peaks are 0.654, 0.342, 0.332, 0.327 and 0.257 nm. The XPS analysis results show that the binding energy of Pb 4f7/2 in the feldspar was between 137.81–138.03 eV. Pb2+ can replace alkali and alkali earth cations in the feldspar structure through ion exchange reaction to form Pb‐feldspar. |
| |
Keywords: | ion exchange Pb-feldspar XRD spectrum XPS analysis |