| 三氟乙酸锂-15-冠醚-5体系电迁移法分离锂同位素 |
| |
| 引用本文： | 黄超驰,孙进贺,张茜,张鹏瑞,汪词明,薛子轩,景燕,贾永忠.三氟乙酸锂-15-冠醚-5体系电迁移法分离锂同位素[J].盐湖研究,2021,29(3):83-89. |
| |
| 作者姓名： | 黄超驰 孙进贺 张茜 张鹏瑞 汪词明 薛子轩 景燕 贾永忠 |
| |
| 作者单位： | 中国科学院青海盐湖研究所,盐湖资源综合高效利用重点实验室,青海 西宁 810008;青海盐湖资源综合利用技术研究开发中心,青海 西宁 810008;中国科学院大学,北京 100049 |
| |
| 基金项目： | 青海省重点研发与转化计划项目(No. 2021-GX-104,2019-GX-169)；中科院青促会(2015351) |
| |
| 摘 要： | 锂同位素(~6Li和~7Li)在核工业中有着重要作用。锂汞齐法是目前唯一实现锂同位素工业化生产的方法,然而由于汞的使用,该方法具有较大的环境风险。开发绿色高效的锂同位素分离方法对国家能源安全具有重要意义。在本论文中,制备了溶解锂盐的冠醚溶液,并以其作为阳极液,施加电场驱动锂离子向阴极液迁移;与溶有15-冠醚-5的锂盐水溶液作为阳极液相比,研究发现在阳极液体系中引入水分子可以促进锂同位素的分离。同时还考察了不同隔膜对锂同位素分离的影响,发现使用强疏水性隔膜时,短时间内有较好的分离效应。
|
| 关 键 词： | 锂同位素分离 15-冠醚-5 电迁移 水合作用 |
| 收稿时间： | 2021/2/2 0:00:00 |
| 修稿时间： | 2021/3/2 0:00:00 |
Separation of Lithium Isotopes by Electromigration with Lithium Trifluoroacetate-15-crown-5 System |
| |
| Huang chaochi,Sun jinhe,Zhang qian,Zhang pengrui,Wang ciming,Xue zixuan,Jin yan and Jia yongzhong.Separation of Lithium Isotopes by Electromigration with Lithium Trifluoroacetate-15-crown-5 System[J].Journal of Salt Lake Research,2021,29(3):83-89. |
| |
| Authors: | Huang chaochi Sun jinhe Zhang qian Zhang pengrui Wang ciming Xue zixuan Jin yan and Jia yongzhong |
| |
| Institution: | Qinghai Institute of Salt Lakes,Qinghai Institute of Salt Lakes,Qinghai Institute of Salt Lakes,Qinghai Institute of Salt Lakes,Qinghai Institute of Salt Lakes,Qinghai Institute of Salt Lakes,Qinghai Institute of Salt Lakes,Qinghai Institute of Salt Lakes |
| |
| Abstract: | Lithium isotopes(6Li and 7Li)play an important role in the nuclear industry.At present,COLEX process is the only method to achieve large-scale industrial application of lithium isotope separation,but it is harmful to the environment because of the mercury involved.The development of a green and efficient lithium isotope separation method is of great significance to national energy security.In this work,a crown ether solution dissolved in lithium salt was prepared and used as anode solution to drive the migration of lithium ions to cathode solution by applying an electric field.Compared with lithium salt solution dissolved with 15-crown-5,it was found that introducing water molecules into the anode solution system could promote the separation of lithium isotopes.The effect of different membrane on the separation of lithium isotopes was also investigated,and it was found that the separation effect was better in a short time when strong hydrophobic membrane was used. |
| |
| Keywords: | lithium isotope separation 15-crown-5 electromigration hydration |
|